A high-strength, tough engineering resin with properties similar to polypropylene (PP). This material provides good impact resistance, excellent surface finish, and is ideal for parts that require some flexibility and durability.
Best for: Tooling applications, manufacturing aids, housings, and functional prototypes requiring ductility and strength.
Specifications:
Note: (TS) refers to the Testing Standard used to measure the specified value.
Color: Black / Clear (TS: N/A)
HDT at 0.455 MPa: 53 C (TS: ASTM D648)
Tensile Stress at Break: 45 MPa (Black), 38 MPa (Clear) (TS: ASTM D638)
Elongation at Break: 100% (Black), 96% (Clear) (TS: ASTM D638)
Young's Modulus: 1,400 MPa (TS: ASTM D638)
Flexural Modulus: 1,400 MPa (Black), 1,300 MPa (Clear) (TS: ASTM D790)
IZOD Impact (Notched): 51 J/m (Black), 72 J/m (Clear) (TS: ASTM D256)
Shore Hardness: 76 D (TS: ASTM D2240)